Influence of initial treatments of aluminium on the morphological features of electrochemically formed alumina membranes
2003
Abstract The fabrication of alumina membranes by electrochemical oxidation of annealed aluminium was investigated. Porous layers were grown in 0.4 M H3PO4 at −1 and 5 °C at different anodising times. The morphology of the outer surface was found to be dependent on temperature and charge density, with both determining the extent of chemical dissolution of the anodic oxide. The inner-surface morphology was found to depend on the applied voltage only. The chemical dissolution rate of anodic oxide grown on annealed aluminium was found to be lower than that formed on unannealed aluminium under otherwise identical conditions. Such a difference in behaviour is explained in terms of a higher finish…
Porosity of anodic alumina membranes from electrochemical measurements
2005
A procedure based on the high-field mechanism of the growth of anodic oxides was developed in order to evaluate the morphological features of porous layers. Since the thickness of the barrier film, separating the porous layer from the metal, does not change during the steady-state growth of an anodic porous layer, the rate of displacement of the metal-oxide interface to the metal direction must be equal to the rate of displacement of the pore base to the oxide direction. As a consequence, porosity can be expressed in terms of the ratio i diss/i ion, where i diss is the dissolution current density at the pore base, and i ion is the ionic current density at the metal-oxide interface. Pore dia…